机械用碳石墨材料类别/型号及技术性能 |
|
型号 Type |
浸渍材料 Impregnated Material |
体积密度 BulkDensity g/cm3 (≥) |
抗折强度 Transverse Strength Mpa(≥) |
抗压强度 Conpressive Strength Mpa (≥) |
肖氏硬度 Hardness Shore (≥) |
气孔率% Porosity (≤) |
热膨胀系数 Coeffcient of Expansion X10-6 /℃ |
使用温度℃ Nax.Suitable Temperature |
| 碳石墨 Pure Carbon Graphite | ||||||||
| XH-M191 | 纯碳石墨 | 1.75 | 85 | 150 | 90 | 1.2 | 600 | |
| XH-M126 | 碳石墨（T) | 1.60 | 40 | 100 | 65 | 12.0 | 400 | |
| XH-M254 | 1.70 | 25 | 45 | 40 | 20.0 | 450 | ||
| XH-M238 | 1.70 | 35 | 75 | 40 | 15.0 | 450 | ||
| 浸渍树脂石墨 Resin-Impregnated Graphite | ||||||||
| XH-M106H |
环氧树脂 Epoxy Resin (H) |
1.75 | 65 | 200 | 85 | 1.5 | 210 | |
| XH-M120H | 1.70 | 60 | 200 | 85 | 1.5 | |||
| XH-M126H | 1.70 | 55 | 160 | 80 | 1.5 | |||
| XH-M180H | 1.80 | 80 | 220 | 90 | 1.5 | |||
| XH-M254H | 1.80 | 35 | 75 | 42 | 1.5 | |||
| XH-M238H | 1.88 | 50 | 105 | 55 | 1.5 | |||
| XH-M106K |
呋喃树脂 Furan Resin (k) |
1.75 | 65 | 200 | 90 | 1.5 | 210 | |
| XH-M120K | 1.70 | 60 | 200 | 85 | 1.5 | |||
| XH-M126K | 1.70 | 60 | 170 | 85 | 1.5 | |||
| XH-M180K | 1.80 | 80 | 220 | 90 | 1.5 | |||
| XH-M238K | 1.85 | 55 | 105 | 55 | 1.5 | |||
| XH-M254K | 1.80 | 40 | 80 | 45 | 1.5 | |||
| XH-M180F |
酚醛树脂 Phenolic Resin (F) |
1.80 | 70 | 220 | 90 | 1.5 | 210 | |
| XH-M106F | 1.75 | 60 | 200 | 85 | 1.5 | |||
| XH-M120F | 1.70 | 55 | 190 | 80 | 1.0 | |||
| XH-M126F | 1.70 | 50 | 150 | 75 | 1.5 | |||
| XH-M238F | 1.88 | 50 | 105 | 55 | 1.5 | |||
| XH-M254F | 1.80 | 35 | 75 | 45 | 1.0 | |||
| 浸渍金属石墨 Metal-Impregnated Graphite | ||||||||
| XH-M120B |
巴氏合金 Babbitt (B) |
2.40 | 60 | 160 | 65 | 9.0 | 210 | |
| XH-M254B | 2.40 | 40 | 70 | 40 | 8.0 | |||
| XH-M106D | 锑 Antimony (D) | 2.20 | 75 | 190 | 70 | 2.5 | 400 | |
| XH-M120D | 2.20 | 70 | 180 | 65 | 2.5 | |||
| XH-M254D | 2.20 | 40 | 85 | 40 | 2.5 | 450 | ||
| XH-M106P | 铜合金 Copper Alloy (P) | 2.60 | 70 | 240 | 70 | 3.0 | 400 | |
| XH-M120P | 2.40 | 75 | 250 | 75 | 3.0 | |||
| XH-M254P | 2.60 | 40 | 120 | 45 | 3.0 | 450 | ||
| 树脂粘合石墨 Resin Graphite | ||||||||
| XH-301 | 热压石墨 | 1.70 | 50 | 98 | 62 | 1.0 | 200 | |
| XH-302 | 热压石墨 | 1.65 | 55 | 105 | 58 | 1.0 | 180 | |
|
机械用碳石墨材料的耐化学腐蚀性能
|
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
|
注：“+”为稳定；“-”为不稳定； “O”为较稳定 。 |
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||